What material group is 316?
What material group is 316?
What material group is 316?
Stainless steel types 1.4401 and 1.4404 are also known as grades 316 and 316L respectively. Grade 316 is an austenitic grade second only to 304 in commercial importance. Stainless steel types 1.4401 and 1.4404 are also known as grades 316 and 3164L respectively.
What is the difference between ss410 and ss304?
Stainless steel 410 has good corrosion resistance, machinability, general purpose blade, valve, mechanical parts, 1 class tableware (spoon, fork, knife, etc.). 304 stainless steel is suitable for food processing, storage and transportation.It has good machining performance and weldability.
What are the properties of 316 stainless steel?
Mechanical Properties and Yield Strength of 316 / 316L Stainless
| Property | Type 316 (S31600) | Type 317 (S31700) |
|---|---|---|
| Yield Strength 0.2% Offset psi MPa | 30,000 205 | 30,000 205 |
| Ultimate Tensile Strength psi MPa | 75,000 515 | 75,000 515 |
| Percent Elongation in 2 in. or 51mm | 40.0 | 35.0 |
| Hardness, Max. Brinell RB | 217 95 | 217 95 |
Which one is better SS316 or ss410?
Because 316 stainless steel contains a lot of molybdenum, so the price of 316 stainless steel is higher than 410 stainless steel. 316 stainless steel is better suited to work in corrosive environments.
Which is better ss410 vs SS316?
316 Stainless Steel also has outstanding welding characteristics. Post-weld annealing is not required when welding thin sections. Stainless Steel 410 is the basic martensitic stainless steel; like most non-stainless steels it can be hardened by a “quench-and-temper” heat treatment.
What is the HRC of 316 stainless steel?
515
Table 2.
| Grade | Tensile Str (MPa) min | Hardness |
|---|---|---|
| Rockwell B (HR B) max | ||
| 316 | 515 | 95 |
| 316L | 485 | 95 |
| 316H | 515 | 95 |